%X This paper aims to fabricated high quality anodic
aluminum oxide (AAO) film by anodization method. AAO pore size,
pore density, and film thickness can be controlled in 10~500 nm,
108~1011, and 1~100 μm. AAO volume and surface area can
be computed based on structural parameters such as thickness, pore
size, pore density, and sample size. Base on the thetorical calculation,
AAO has 100 μm thickness with 15 nm, 60 nm, and 500 nm pore
diameters AAO surface areas are 1225.2 cm2, 3204.4 cm2, and 549.7
cm2, respectively. The large unit surface area which is useful for
adsorption application. When AAO adsorbed pH indictor of
bromphenol blue presented a sensitive pH detection of solution
change. This testing method can further be used for the precise
measurement of biotechnology, convenience measurement of
industrial engineering.