Springback Property and Texture Distribution of Grained Pure Copper
Abstract:
To improve the material characteristics of single- and poly-crystals of pure copper, the respective relationships between crystallographic orientations and microstructures, and the bending and mechanical properties were examined. And texture distribution is also analyzed. A grain refinement procedure was performed to obtain a grained structure. Furthermore, some analytical results related to crystal direction maps, inverse pole figures, and textures were obtained from SEM-EBSD analyses. Results showed that these grained metallic materials have peculiar springback characteristics with various bending angles.
Keywords:
Pure Copper, Grain Refinement, Environmental Materials, SEM-EBSD Analysis, Texture, Microstructure
5
16615
In-Situ EBSD Observations of Bending for Single-Crystalline Pure Copper
Abstract:

To understand the material characteristics of singleand poly-crystals of pure copper, the respective relationships between crystallographic orientations and microstructures, and the bending and mechanical properties were examined. And texture distribution is also analyzed. A bending test is performed in a SEM apparatus and while its behaviors are observed in situ. Furthermore, some analytical results related to crystal direction maps, inverse pole figures, and textures were obtained from EBSD analyses.

Keywords:
Pure Copper, Bending, Single Crystal, SEM-EBSD Analysis, Texture, Microstructure
4
9999186
Statistical Estimation of Spring-back Degree Using Texture Database
Abstract:

Using a texture database, a statistical estimation of spring-back was conducted in this study on the basis of statistical analysis. Both spring-back in bending deformation and experimental data related to the crystal orientation show significant dispersion. Therefore, a probabilistic statistical approach was established for the proper quantification of these values. Correlation was examined among the parameters F(x) of spring-back, F(x) of the buildup fraction to three orientations after 92° bending, and F(x) at an as-received part on the basis of the three-parameter Weibull distribution. Consequent spring-back estimation using a texture database yielded excellent estimates compared with experimental values.

Keywords:
Bending, Spring-back, Database, Crystallographic Orientation, Texture, SEM-EBSD, Weibull distribution, Statistical analysis.
3
10000016
In-situ Observations Using SEM-EBSD for Bending Deformation in Single-Crystal Materials
Abstract:

To elucidate the material characteristics of single crystals of pure aluminum and copper, the respective relations between crystallographic orientations and microstructures were examined, along with bending and mechanical properties. The texture distribution was also analysed. Bending tests were performed in a SEM apparatus while its behaviors were observed. Some analytical results related to crystal direction maps, inverse pole figures, and textures were obtained from electron backscatter diffraction (EBSD) analyses.

Keywords:
Pure aluminum, Pure copper, Single crystal, Bending, SEM-EBSD analysis, Texture, Microstructure.
2
10008689
SEM-EBSD Observation for Microtubes by Using Dieless Drawing Process
Abstract:

Because die drawing requires insertion of a die, a plug, or a mandrel, higher precision and efficiency are demanded for drawing equipment for a tube having smaller diameter. Manufacturing of such tubes is also accompanied by problems such as cracking and fracture. We specifically examine dieless drawing, which is less affected by these drawing-related difficulties. This deformation process is governed by a similar principle to that of reduction in diameter when pulling a heated glass tube. We conducted dieless drawing of SUS304 stainless steel microtubes under various conditions with three factor parameters of heating temperature, area reduction, and drawing speed. We used SEM-EBSD to observe the processing condition effects on microstructural elements. As the result of this study, crystallographic orientation of microtube is clear by using SEM-EBSD analysis.

Keywords:
Microtube, dieless drawing, IPF, inverse pole figure, GOS, grain orientation spread, crystallographic analysis.
1
10008690
Texture Observation of Bending by XRD and EBSD Method
Abstract:

The crystal orientation is a factor that affects the microscopic material properties. Crystal orientation determines the anisotropy of the polycrystalline material. And it is closely related to the mechanical properties of the material. In this paper, for pure copper polycrystalline material, two different methods; X-Ray Diffraction (XRD) and Electron Backscatter Diffraction (EBSD); and the crystal orientation were analyzed. In the latter method, it is possible that the X-ray beam diameter is thicker as compared to the former, to measure the crystal orientation macroscopically relatively. By measurement of the above, we investigated the change in crystal orientation and internal tissues of pure copper.

Keywords:
Bending, electron backscatter diffraction, X-ray diffraction, microstructure, IPF map, orientation distribution function.